KAJIAN EKSPERIMENTAL TENSILE PROPERTIES KOMPOSIT POLIESTER BERPENGUAT SERAT KARBON SEARAH HASIL MANUFAKTUR VACUUM INFUSION SEBAGAI MATERIAL STRUKTUR LSU
Abstract
Vacuum infusion is a manufacturing method to improve mechanical properties of composite. Before apply this in LSU structure, it should be experimented using tensile test to know mechanical properties of the composite. Tensile test is an experimental to know tensile strength, modulus of elasticity, and failure modes of composite. Experimental process of CFRP composite using unidirectional carbon fiber and polyester matrix was done using vacuum infusion technology, strart from specimens preparation until testing steps. Manufacturing results gave the values of composite density and thickness; mass and volume fraction of fiber and matrix materials. Specimens and testing process are refer to ASTM D3039 tensile test standard for composite matrix polymers. The testing results showed 1011.67 MPa ultimate tensile strength, 59074.96 MPa modulus of elasticity, and SGV (long spliting, gage, various) failure mode .
Â
ABSTRAK
Vacuum infusion merupakan salah satu metode manufaktur yang digunakan untuk meningkatkan sifat mekanik komposit. Untuk mengaplikasikan metode ini dalam pembuatan struktur LAPAN Surveillance UAV (LSU), perlu diketahui terlebih dahulu sifat mekanik dari komposit hasil metode ini secara eksperimen. Salah satu eksperimen yang dilakukan yaitu pengujian tarik untuk mendapatkan tensile strength, modulus elastisitas, dan failure mode yang terjadi pada komposit. Eksperimen dilakukan terhadap komposit CFRP menggunakan material serat karbon searah (UD) 0â° dan matriks poliester dibuat dengan metode vacuum infusion mulai dari tahap preparasi sampai tahap pengujian. Dari hasil manufaktur didapat nilai densitas dan ketebalan komposit serta fraksi massa dan fraksi volume material penyusun komposit. Spesimen dan proses pengujian mengikuti standar ASTM D3039 yang merupakan standar pengujian tarik untuk komposit dengan matriks polimer. Hasil pengujian menunjukkan nilai ultimate tensile strength 1011,67 MPa, modulus elastisitas 59074,96 MPa, dan failure mode SGV (Long Spliting, Gage, Various).
Keywords
Full Text:
PDFReferences
Abdurohman, K, 2105. Uji Ketebalan Komposit
dengan Metode Vacuum Infusion, TN11,
LAPAN.
Bakir, B. dan H. Hasim, 2013. Effect of Fiber
Orientation for Fiber Glass Reinforced
Composite Material on Mechanical
Properties, International Journal of
Mining, Metallurgy & Mechanical
Engineering (IJMMME) Volume 1, Issue
(2013) ISSN 2320-4052.
Blas, F. and I. Fernandez, 2001. Mechanical
Characterisation of Carbon/Epoxy
Composite Materials Manufactured by
Resin Film Infusion Method with
Stitching Reinforcement, STO Meeting
Proceedings, RTO-MP-069(II).
Chen, J.C; Wu, C.M; Pu, F.C; and C.H. Chiu, 2011.
Fabrication and Mechanical Properties of
Self-reinforced Poly(ethylene Terephthalate)
Composites, eXPRESS Polymer Letters
(Journal: ISSN 1788-618X) Vol.5, No.3
(2011) 228–237.
Faizal, M.A; Beng, Y.K; and K.N. Dalimin, 2011.
Tensile Property of Hand Lay-Up PlainWeave
Woven E-Glass/Polyester
Composite: Curing Pressure and Ply
Arrangement Effect, Borneo Science,
The Journal of Science & Technology,
ISSN: 2231-9085.
Goren, A. dan Atas, C., 2011. Manufacturing of
Polymer Matrix Composites Using
Vacuum Assisted Resin Infusion
Molding, International Scientific
Journal, World Academy of Materials
and Manufacturing Engineering,
Volume 34 Issue 2, December 2008,
Pages 117-120.
Jweeg, M.J; Hammood, A.S; and M. AlWaily,
Experimental and Theoretical
Studies of Mechanical Properties for
Reinforcement Fiber Types of Composite
Materials, International Journal of
Mechanical & Mechatronics
Engineering IJMME-IJENS Vol:12.
Murugan, R; Ramesh, R; Padmanabhan, K, 2014.
Investigation on Static and Dynamic
Mechanical Properties of Epoxy Based
Woven Fabric Glass/Carbon Hybrid
Composite Laminate, Procedia Engineering
( 2014 ) 459 – 468, Elsevier Ltd.
Paiva, J.M.F; Meyer, S; and M.C. Rezende,
Comparison of Tensile Strength of
Different Carbon Fabric Reinforced
Epoxy Composites, Materials Research,
Ibero-American Journal of Material Vol.
, No. 1, 83-89.
Pegoretti, A; Zanolli A; and C. Migliaresi, 2006.
Preparation and Tensile Mechanical
Properties of Unidirectional Liquid
Crystalline Single-Polymer Composite,
Composites Science and Technology 66
(2006) 1970-1979, Elsevier Ltd.
Quinn, J.A., 2002. Composite Design Manual
Third Edition, James Quinn Associates
Ltd.
Torabizadeh, M.A., 2013. Tensile, Compressive
and Shear Properties of Unidirectional
Glass/Epoxy Composites Subjected to
Mechanical Loading and Low Temperature
Services, Indian Journal of Engineering
& Materials Sciences, Vol. 20, 299-309.
Wang, P; Drapier, S; Molimard, J; Vautrin, A;
and J.C. Minni, 2011. Numerical and
Experimental Analyses of Resin Infusion
Manufacturing Processes of Composite
Materials, Journal of Composite
Materials 46(13) 1617-1631.
Wang, P; Molimard, J; Drapier, S; Vautrin, A;
and J.C. Minni, 2011. Monitoring the
Resin Infusion Manufacturing Processes
Under Industrial Environment Using
Distributed Sensors, Journal of
Composite Materials 46(6) 691-706.
Yamashita, M; Takeda, F; Sakagawa, T; Kimata,
F; and Y. Komori, 2008. Development of
Advanced Vacuum-assisted Resin
Transfer Molding Technology for Use in
an MRJ Empennage Box Structure,
Technical Review Vol. 45 No. 4,
Mitsubishi Heavy Industries, Ltd.
Yeung, K.K.H. and K.P. Rao, 2014. Mechanical
Properties of Boron and Kevlar-49
Reinforced Thermosetting Composites
and Economic Implications, Journal of
Engineering Science, Vol. 10, 19–29.
Refbacks
- There are currently no refbacks.